Research Progress on String Erosion
During Massive Sand Fracturing

doi:10.12388/j.issn.1673-2677.2022.03.011

Abstract

Abstract: Massive sand fracturing is a necessary means for the development of unconventional oil and gas resources，as well as an important cause for the failure of downhole pipe strings and tools due to erosion wear. Targeted at this problem，the erosion theories and main research conclusions proposed by foreign scholars based on different materials are reviewed comprehensively，and the derivative researches into basic erosion theories conducted in China are summarized. Combined with the actual technological conditions，the main causes of serious erosion of pipe string in the process of sand fracturing are expounded. With respect to the pipe string structures and fracturing tools that are likely to be eroded in the process of massive sand fracturing，the research progress is introduced. Current research difficulties and future research direction of fracturing string erosion are pointed out，which is of important reference value and engineering significance for protecting the fracturing string against erosion and the wellbore integrity，and improving the development effect of unconventional oil and gas resources.

Key words: sand fracturing, erosion, fracturing string, fracturing technology, erosion theory, erosion environment

摘要： 大规模加砂压裂是非常规油气资源开采的必要手段，也是导致井下管柱和工具发生冲蚀磨损失效的重要原因。针对这一问题，综合评述了国外学者基于不同材料研究提出的冲蚀理论以及主要研究结论，并总结了国内对于基础冲蚀理论做出的衍生研究。结合实际工艺工况阐述了加砂压裂过程中管柱严重冲蚀的主要原因；针对大规模加砂压裂过程中易被冲蚀的管柱结构和压裂工具介绍了研究进展。指出了当前压裂管柱冲蚀的研究难点及未来的研究方向，对压裂管柱的冲蚀防护问题，保护井筒完整性和提高非常规油气资源的开发效果有重要的参考价值和工程意义。

关键词: 加砂压裂, 冲蚀, 压裂管柱, 压裂工艺, 冲蚀理论, 冲蚀环境

CLC Number:

TE38','1');return false;" target="_blank"> TE38

ZHANG Sisong, ZENG Dezhi, PAN Yuting, TIAN Gang, YU Huiyong, SHI Shanzhi.

Research Progress on String Erosion During Massive Sand Fracturing [J]. Xinjiang Oil & Gas, 2022, 18(3): 65-72.

张思松, 曾德智, 潘玉婷, 田刚, 于会永, 石善志.

大规模加砂压裂管柱冲蚀研究进展 [J]. 新疆石油天然气, 2022, 18(3): 65-72.

References

［1］董建蓉，许朝阳，乐彦婷，等. 新型“油公司”模式下页岩气生产全产业链视角工业增加值计算新方法［J］. 天然气工业，2022，42（2）：151-155.

［2］李海涛，罗红文，向雨行，等. DTS/DAS技术在水平井压裂监测中的应用现状与展望［J］. 新疆石油天然气，2021，17（4）：62-73.

［3］李小刚，张博宁，陈更生，等. 基于生命周期理论的美国页岩气产业发展启示［J］. 天然气工业，2021，41（12）：81-89.

［4］练章华，牟易升，张强. 极端条件下气井油管柱振动力学行为的有限元分析［J］. 新疆石油天然气，2021，17（3）：59-66.

［5］李国欣，朱如凯. 中国石油非常规油气发展现状、挑战与关注问题［J］. 中国石油勘探，2020，25（2）：1-13.

［6］KLIAFAS Y，HOLT M. Measurements of a turbulent air-solid two-phase flow in a 90° bend［J］. Experiments in Fluids，1987，5（2）：73-85.

［7］MAZDAK P，RONALD V，NETAJI K，et al. Ultrasonic measurements of sand particle erosion in gas dominant multiphase churn flow in vertical pipes［J］. Wear，2015（328-329）：401-413.

［8］刘凯新，郑伟杰，戴丽娅，等. X井区低成本体积压裂技术探索及实践［J］. 新疆石油天然气，2022，18（1）：80-85.

［9］昝林峰，孙小喆，李晓平，等. 基于LedaFlow和Fluent的冲蚀临界速率研究［J］，石油与天然气化工，2020，49（1）：67-71、81.

［10］樊艳芳，李少安，曾德智，等. 应急放喷工况井下管柱冲蚀行为研究［J］. 特种油气藏，2020，27（1）：169-174.

［11］曹学文，李星標，樊茵，等. 固体颗粒冲蚀理论与试验研究进展［J］. 油气储运，2019（3）：251-257.

［12］彭东华，董绍华，张行，等. 冲蚀磨损在油气管道行业的研究进展［J］. 油气储运，2021，40（7）：730-741.

［13］FINNIE I. The mechanism of erosion of ductile metals［C］. 3rd US National Congress of Applied Mechanics，NewYork，USA，1958：527-532.

［14］FINNIE I，MCFADDEN D H. On the velocity dependence of the erosion of ductile metals by solid particles at low angles of incidence［J］. Wear，1978，48（1）：181-190.

［15］BITTER J G A. A study of erosion phenomena：Part II［J］. Wear，1963，6（3）：169-190.

［16］TILLY G P. A two stage mechanism of ductile erosion［J］. Wear，1973，23（1）：87-96.

［17］TILLY G P. Erosion Caused by impact of solid particles［J］. Wear，1979，13（3）：287-319.

［18］FLEMING J R，SUH N P. Mechanics of crack propagation in delamination wear［J］. Wear，1977，44（1）：39-56.

［19］EVANS A G，GULDEN M E，ROSENBLATT M. Impact damage in brittle materials in the elastic-plastic response regime［J］. Proceedings of the Royal Society of London. Series A，Mathematical and Physical. 1978，361（1706）：343-365.

［20］HUTCHINGS I M. A model for the erosion of metals by spherical-particles at normal incidence［J］. Wear，1981，70（3）：269-281.

［21］LEVY A，CHIK P. The effects of erodent composition and shape on the erosion of steel［J］. Wear，1983，89（2）：151-162.

［22］张永清，陈登崖，顾佩兰. 韧性材料冲蚀磨损的机理研究［J］. 上海交通大学学报，1989，23（3）：100-105.

［23］林福严，邵荷生. 软磨料冲蚀磨损机理的研究［J］. 水利电力机械，1990，1（6）：17-21.

［24］林福严，邵荷生. 低角度冲蚀磨损机理的研究［J］. 中国矿业大学学报，1991，20（3）：29-34.

［25］刘新宽，方其先. 液固两相流冲刷腐蚀研究［J］. 华电技术，1998，5（5）：33-35.

［26］刘新宽，方其先. 两种不锈钢冲刷腐蚀的研究［J］. 化工机械，1998，35（1）：12-15.

［27］郑玉贵，姚治铭，柯伟. 流体力学因素对冲刷腐蚀的影响机制［J］. 腐蚀科学与防护技术，2000，12（1）：37-40.

［28］董刚，张九渊，白万金，等. 几种工程材料的冲蚀行为的研究［J］. 材料科学与工程学报，2004，22（6）：909-913.

［29］MOJID M R，NEGASH B M，ABDULELAH H. et al. A state-of-art review on waterless gas shale fracturing technologies［J］. Journal of Petroleum Science and Engineering，2021（196）：108048.

［30］刘奎，王宴滨，高德利，等. 页岩气水平井压裂对井筒完整性的影响［J］. 石油学报，2016，37（3）：406-414.

［31］马新华，谢军. 川南地区页岩气勘探开发进展及发展前景［J］. 石油勘探与开发，2018，45（1）：161-169.

［32］谢军. 长宁—威远国家级页岩气示范区建设实践与成效［J］. 天然气工业，2018，38（2）：1-7.

［33］郑有成，范宇，雍锐，等. 页岩气密切割分段+高强度加砂压裂新工艺［J］. 天然气工业，2019，39（10）：76-81.

［34］丁宇奇，兰乘宇，刘巨保，等. 分层压裂管柱冲蚀特性数值模拟与实验分析［J］. 石油钻采工艺，2017，39（2）：231-236.

［35］张旭昀，压裂工况下工具材料及表面涂层冲刷磨损机理研究［D］. 黑龙江大庆：东北石油大学，2013.

［36］刘合，刘伟，王素玲，等. 水平井体积压裂套管失效机制研究现状及趋势初探［J］. 中国石油大学学报：自然科学版，2020，44（6）：53-62.

［37］董云龙，唐世忠，牛艳花，等. 水平井套管固井滑套分段压裂完井存在问题及对策［J］. 石油钻采工艺，2013，35（1）：28-30.

［38］魏辽，韩峰，陈涛，等. 套管固井滑套冲蚀磨损模拟分析与试验研究［J］. 石油钻探技术，2014，42（3）：108-111.

［39］张晓东，陈龙. 基于冲蚀磨损理论的压裂滑套导流角度数研究［J］. 中国科技论文，2018，13（22）：2586-2591.

［40］曾杰，朱海燕，张维，等. 三层式套管滑套设计及其冲蚀规律分析［J］. 机械设计与研究，2018，34（2）：181-186.

［41］孙丽丽. 水力压裂工况下典型材质损伤行为及机理研究［D］. 黑龙江大庆：东北石油大学. 2015.

［42］王尊策，徐艳，闫月娟，等. 偏心工况下水平井压裂管柱喷砂器冲刷磨损数值模拟［J］. 东北石油大学学报，2020，44（5）：98-107.

［43］钟林，冯桂弘，朱和明，等. 压裂球座结构优化分析及耐冲蚀研究［J］. 表面技术，2021，50（6）：213-219.

［44］丁坤，李建民，杨文新，等. 压裂液对水平井滑套球座冲蚀磨损的数值模拟［J］. 石油机械，2014，42（12）：75-78.

［45］向正新，李思行，钱利勤，等. 压裂球座冲蚀磨损规律研究和结构优化［J］. 工程设计学报，2017，24（5）：555-562.

［46］马明新，王绍先，侯婷，等. 分段压裂球座耐冲蚀性能评价［J］. 石油机械，2016，44（1）：67-70.

［47］李勇明，陈曦宇，赵金洲，等. 射孔孔眼磨蚀对分段压裂裂缝扩展的影响［J］. 天然气工业，2017，37（7）：52-59.

［48］CRUMP J B，CONWAY M W. Effects of perforation-entry friction on bottomhole treating analysis［J］. Journal of Petroleum Technology，1988，40（8）：1041-1048.

［49］刘雁蜀，秦龙，王治国，等. 套管压裂过程中射孔孔眼冲蚀数值模拟［J］. 石油机械，2015，43（9）：66-69.

［50］曾德智，张思松，田刚，等. 加砂压裂过程中套管孔眼抗冲蚀性能分析［J］. 表面技术，2022，51（6）：204-213.

［51］LONG G B，LIU S X，XU G S，et al. A perforation-erosion model for hydraulic-fracturing applications［J］. SPE Production & Operations，2018，33（4）：770-783.

［52］LONG G B，XU G S. The effects of perforation erosion on practical hydraulic-fracturing［J］. SPE Journal，2017，22（2）：645-659.

Research Progress on String Erosion During Massive Sand Fracturing

大规模加砂压裂管柱冲蚀研究进展

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 0

Recommended Articles

Metrics